- Home
- About Us
- Events
- FluoroKote#1®
-
Industrial Coating Services
- Fluoropolymer Coatings
- Xylan Coatings
- Molybdenum Disulfide Coatings
- PTFE Coatings
- Epoxy Coatings, Air Dry
- Phosphate Coatings
- Epoxy Coatings, Thermal Cure
- Phenolic Coatings
- Polyurethane Coatings
- Inorganic Zinc Coatings
- Polyphenylene Sulfide / Ryton
- FEP Coating
- PVDF / Kynar Coatings
- ECTFE / Halar Coatings
- Ceramic Epoxy Coating
- Coating Applications
- Fastener Coatings
- Coating Specification
- Industries Served
- Support
- Contact Us
Corrosion Resistant Coating Test Data
- Use Temperatures: -100° to 500°F
- Corrosion Resistance: Salt Spray (ASTM B117) ...up to 4,000 hrs (Nuts not frozen)
- Pencil Hardness: 5H-6H (ASTM D3363-92A)
- Kinetic Friction Coefficient: 0.06-0.08
- Thickness: nominal 0.001" (1 mil)
- Impact: 160 in. lb. (ASTM D2794-93)
- Adhesion: 5B (ASTM D3359-95)
- Dielectric Strength: 500 volts per mil
- Elongation: 35%-50%
- Tensile Strength: 4,000 psi
- Operating Pressure: Up to 100,000 psi
- Kesternich Test: Nuts not frozen after 30+ cycles (DIN 50018)
- Thread Fit: Over tapping of nuts 0.010" (Recommended)
Salt Spray Resistance & Other Corrosion Resistance Details:
ASTM | TEST | DURATION | RESULTS |
---|---|---|---|
D1308 | Muriatic Acid 31% HCL | 24 Hours | No Effect |
D1308 | Sulfuric Acid 93% H2SO4 | 24 Hours | No Effect |
D1308 | Caustic Soda 50% NaOH | 24 Hours | No Effect |
D1308 | Methyl Ethyl Ketone MEK | 24 Hours | No Effect |
B117 | Salt Fog | 2,000 Hours | No Effect |